Productdetails:
Betalen & Verzenden Algemene voorwaarden:
|
| Naam: | De Bar van de magnesiumlegering | Model: | Az31b Az61a Az91D |
|---|---|---|---|
| Vorm: | bar/staaf | Oppervlakte: | Vlotte Oppervlakte |
| Materiaal: | Magnesium, Magnesiumlegering | Zuiverheid: | >98% |
| Toepassing: | Autodelen of 3C-Producten | Chemische Samenstelling: | Mg, Al, Zn, Mn, Fe, Cu |
| Kleur: | Zilver | Techniek: | Koudgewalst gerold /hot |
| Levertijd: | 10 -30 dagen | ||
| Hoog licht: | 3C de Legeringsstaaf van het productenaz91d Magnesium,De autodelen AZ61A Staaf van de Magnesiumlegering,3C de Legeringsbar van het productenaz31b Magnesium |
||
De Legeringsstaaf/Bar van het Az31baz61a Az91D Magnesium voor Autodelen of 3C-Producten
Details:
|
Productnaam
|
De bar van de magnesiumlegering
|
|
Materiële rang
|
AZ31B/ZK60A/AZ91D/AZ61A/AZ80A/WE43
|
|
Levertijd
|
3 tot 25 werkdagen
|
|
Norm
|
ASTM B265, ASME SB265, AMS4911, ASTM F136, ASTM F67
|
|
Vorm
|
bar, staaf
|
|
Pakket
|
Houten pallet of volgens het verzoek van de klant
|
|
Afmetingen
|
Dikte: 0.3mm200mm
|
|
Breedte: aangepaste Max.width 3000mm
|
|
|
Lengte: Aangepast
|
De Chemische Samenstelling van de magnesiumlegering:
|
Model
|
Chemische Component (%):
|
||||||
|
Type
|
Mg
|
Al
|
Zn
|
Mn
|
Si
|
Fe
|
Cu
|
|
AZ31B
|
overblijvend
|
2.5-3.5
|
0.60-1.4
|
0.20-1.0
|
≤0.08
|
≤0.003
|
≤0.001
|
|
AZ61A
|
overblijvend
|
5.8-7.2
|
0.40-1.5
|
0.15-0.50
|
≤0.10
|
≤0.005 |
≤0.005
|
|
AZ80A
|
overblijvend
|
7.8-9.2
|
0.20-0.80
|
0.12-0.50
|
≤0.10
|
≤0.005
|
≤0.005
|
|
AZ91D
|
overblijvend
|
8.5-9.5
|
0.45-0.90
|
0.17-0.40
|
≤0.08
|
≤0.004
|
≤0.001
|
|
Magnesiumlegering
|
Mechanisch Bezit
|
Toepassing
|
||
|
ASTM
|
treksterkte (N/MM2)
|
Opbrengststerkte (N/mm)
|
Verlenging
|
--
|
|
AZ31B
|
230~290
|
170~210
|
10~24
|
Standaarduitdrijvingslegering
|
|
AZ61A
|
270~390
|
190~240
|
9~15
|
Uitdrijvingslegering met hoge weerstand
|
|
AZ80A
|
330~360
|
230~250
|
8~10
|
Uitdrijvingslegering met hoge weerstand
|
Dichtheid: 1.8
Coëfficiënt van thermische uitbreiding: 26.8 x 10-6K-1
Specifieke hitte: 1040 jkg-1k-1
Warmtegeleidingsvermogen: 76.9Wm-1k-1
Elektroweerstandsvermogen: 92nΩm
Modulus van elasticiteit: 45 x 109Pa
Poissonsverhouding: 0,35
Smeltende waaier: 566 - 632°C.
Prestatietestgegevens:
| Nr. | Model | Beproevingsomstandigheid | Ontbindingstarief mg (cm2*h)) |
Sterkte van uitbreiding (MPa) | Opbrengststerkte (MPa) | Verlenging (%) |
Hardheid (HB) |
| 1 | HB006 | 93℃/3%KCl | 50-70 | ≥370 | ≥260 | ≥2.5 | ≥90 |
| 2 | HB006A | 93℃/3%KCl | 50-70 | ≥310 | ≥220 | ≥6.0 | ≥75 |
| 3 | HB008 | 93℃/3%KCl | 40-60 | ≥400 | ≥300 | ≥4.0 | ≥100 |
| 4 | HB008B | 93℃/3%KCl | 40-60 | ≥370 | ≥270 | ≥5 | ≥100 |
| 5 | HB008C | 93℃/3%KCl | 40-60 | ≥310 | ≥220 | ≥15 | ≥85 |
| 6 | HB012 | 93℃/3%KCl | 40-60 | ≥400 | ≥300 | ≥3.0 | ≥100 |
| 7 | HB011 | 93℃/3%KCl | 15-35 | ≥420 | ≥300 | ≥3.0 | ≥100 |
| 8 | HB016 | 93℃/3%KCl | 35-55 | ≥280 | ≥180 | ≥15 | ≥60 |
| 9 | HB017 | 93℃/3%KCl | 40-50 | ≥200 | ≥140 | ≥17 | ≥55 |
| 10 | HB018K | 50℃/0.84KCl | 50-70 | ≥240 | ≥170 | ≥12 | ≥55 |
| 11 | HB018 | 50℃/0.84KCl | 30-50 | ≥230 | ≥170 | ≥12 | ≥55 |
| 12 | HB010 | 93℃/3%KCl | 15-35 | ≥190 | ≥120 | ≥30 | ≥45 |
| 13 | HB022 | 43℃/0.05%KCl | 50-60 | ≥300 | ≥200 | ≥5.0 | ≥75 |
| 14 | HB023 | 43℃/0.05%KCl | 20-40 | ≥280 | ≥200 | ≥7.5 | ≥65 |
| 15 | HB024 | 43℃/0.05%KCl | 50-70 | ≥260 | ≥220 | ≥5 | ≥60 |
| 16 | HB013A | 43℃/0.05%KCl | 80-100 | ≥260 | ≥230 | ≥3.5 | ≥75 |
| 17 | HB025 | 50℃/0.84%KCl | 90-110 | ≥275 | ≥200 | ≥12 | ≥65 |
| 18 | HB026 | 93℃/3%KCl | 20-40 | ≥450 | ≥350 | ≥3.0 | ≥110 |
| 19 | HB808 | 50℃/0.84%KCl | 50-70 | ≥370 | ≥260 | ≥3.0 | ≥100 |
| 20 | HB019 | 50℃/0.84KCl | 45-65 | ≥230 | ≥180 | ≥12.0 | ≥55 |
| 21 | HB055 | 93℃/3%KCl | 130-150 | ≥220 | ≥160 | ≥12.0 | ≥55 |
| 22 | HB035 | 93℃/3%KCl | 50-100 | ≥100 | ≥60 | ≥42.0 | ≥35 |
| 23 | HBMM6 | 50℃/0.84%KCl | 70-100 | ≥260 | ≥230 | ≥10.0 | ≥60 |
| 24 | HBMM7 | 50℃/0.84%KCl | 90-120 | ≥270 | ≥240 | ≥9.0 | ≥65 |
| 25 | HBMM8 | 93℃/3%KCl | 100-150 | ≥280 | ≥250 | ≥5.0 | ≥65 |
Voordeel van Hilbo-Bedrijf:
De volledige waaier van producttypes, verzekert productiecapaciteit
Wij ave gingen het gieten, uitdrijving, smeedstuk, het rollen, het gieten verwerkingsproductielijn en precisie het testen materiaal vooruit. Kan een verscheidenheid van types van magnesiumlegering en van de magnesiumlegering producten veroorzaken, en ontwikkelde een magnesiumlegering uitgedreven blad met hoge weerstand. Door de reiniging van gewoon magnesium, kan het magnesium tot 99,99% van hoge zuiverheid worden opgeheven.
1. Diverse grootte van magnesiummateriaal in voorraad
2. Directe fabriek
3. Strikte inspectie en snelle levering (MTC zal worden vastgemaakt)
4. De korte levering en de grootte kunnen zijn customzied 5.Quite-beroeps met grote ervaring
Kostenvoordeel
Magnesiumlegering het gieten de productie kan aangepast als uw vereiste. het technische die proces is groot, uitdrijvingsproductie voor een verscheidenheid van bar, geen behoefte wordt vereist om in het buitenland te kopen van, uitdrijvings vormende producten is het gemakkelijke vormen, laag energieverbruik, die productiekosten bewaren.
Workshop:
Het testen Materiaal
Onze Diensten:
1. Kleine beschikbare ordehoeveelheid
2. Professioneel techniekteam en verkoopteam
3. Betaling: T/T & Western Union
4. OEM/ODM Supporttable
5. Vrije verstrekte steekproeven
6. Concurrerende prijs en hoog - kwaliteit
Certificaat:
Wij hebben de certificaten van ISO9001 en ISO14001-bereikt, en verbeteren het beheersysteem van de ondernemingskwaliteit gestandaardiseerd.
FAQ:
Contactpersoon: Miss. Emily shi
Tel.: +86 13714725615
Fax: 86-0769-82385085
AZ31B-H24 van het de Plaat Dikke Magnesium van de magnesiumlegering het Bladplak Met hoge weerstand
Multifunctionele Noodsituatie 2 in 1 Mag verspert Brandaanzet 5,5 x 3 x 0,2 Duim